2219-T62 Sheet and plate: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Aluminum |
| Alloy / temper / form | 2219 / T62 / Sheet and plate |
| Specifications | AMS 4031 & AMS-QQ-A-250/30 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 3.2.8.0, Table 3.2.8.0(b) (pdf page 168 of the chapter file) |
| Dimension bands | 1 |
| Density | 2851 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.020–2.000 in (0.508–50.8 mm) | ||
|---|---|---|---|
| Specification | AMS 4031 & AMS-QQ-A-250/30 | ||
| Basis | A | B | |
| Ftu, MPa | L | 372.3 | 379.2 |
| LT | 372.3 | 379.2 | |
| Fty, MPa | L | 248.2 | 255.1 |
| LT | 248.2 | 255.1 | |
| Fcy, MPa | L | 255.1 | 268.9 |
| LT | 255.1 | 262 | |
| Fsu, MPa | L | 213.7 | 220.6 |
| LT | 213.7 | 220.6 | |
| Fbru (e/D = 1.5), MPa | L | 579.2 | 586.1 |
| LT | 579.2 | 586.1 | |
| Fbru (e/D = 2.0), MPa | L | 737.7 | 751.5 |
| LT | 737.7 | 751.5 | |
| Fbry (e/D = 1.5), MPa | L | 427.5 | 441.3 |
| LT | 427.5 | 441.3 | |
| Fbry (e/D = 2.0), MPa | L | 544.7 | 558.5 |
| LT | 544.7 | 558.5 | |
| E, GPa | 72.39 | 72.39 | |
| Ec, GPa | 74.46 | 74.46 | |
| G, GPa | 27.58 | 27.58 | |
| ν | 0.33 | 0.33 | |
| ρ, kg/m³ | 2851 | 2851 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Strength allowables at temperature, percent of room temperature
| °C | F_tu | F_ty |
|---|---|---|
| -184 | 119.7 | 116.3 |
| -129 | 109.3 | 108.4 |
| -73 | 104.9 | 104.6 |
| -18 | 102.5 | 102 |
| 38 | 100.3 | 98.8 |
| 93 | 94.6 | 93.7 |
| 149 | 81.3 | 83.8 |
| 204 | 63.8 | 67.3 |
| 26 | 45.7 | 50.7 |
| 316 | 31.6 | 36.9 |
| 371 | 19.2 | 22.2 |
| 427 | 7.8 | 9.1 |
Factors in percent of the room-temperature allowable.
Other 2219 Tables
- 2219-T81 Sheet and plate (Table 3.2.8.0(b))
- 2219-T851 Sheet and plate (Table 3.2.8.0(b))
- 2219-T8511 Extruded shapes (Table 3.2.8.0(d))
- 2219-T852 Hand Forging (Table 3.2.8.0(c))
- 2219-T87 Plate (Table 3.2.8.0(b))
- 2219-T87 Sheet (Table 3.2.8.0(b))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.