Tools › Materials › Aluminum › 2219-T87 Plate

2219-T87 Plate: MIL-HDBK-5J Design Allowables

show SI units (MPa, GPa, kg/m³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Material class	Aluminum
Alloy / temper / form	2219 / T87 / Plate
Specifications	AMS-QQ-A-250\30
Handbook	MIL-HDBK-5J, 31 January 2003, section 3.2.8.0, Table 3.2.8.0(b) (pdf page 170 of the chapter file)
Dimension bands	6
Density	0.103 lb/in3

Design Mechanical and Physical Properties (room temperature)

As printed in the handbook table. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Dimension band		0.250–1.000 in		1.001–1.500 in		1.501–2.000 in		2.001–3.000 in		3.001–4.000 in		4.001–5.000 in
Specification		AMS-QQ-A-250\30		AMS-QQ-A-250\30		AMS-QQ-A-250\30		AMS-QQ-A-250\30		AMS-QQ-A-250\30		AMS-QQ-A-250\30
Basis		A	B	A	B	A	B	A	B	A	B	A	B
F_tu, ksi	L	63	64	63	64	63	64	63	64	61	62	…	…
	LT	64	65	64	65	64	65	64	65	62	63	61	62
	ST	…	…	…	…	59	60	56	57	52	53	…	…
F_ty, ksi	L	50	51	50	51	50	51	50	51	49	50	…	…
	LT	51	52	51	52	51	52	51	52	51	51	49	50
	ST	…	…	…	…	51	52	50	51	48	49	…	…
F_cy, ksi	L	51	52	51	52	51	52	…	…	…	…	…	…
	LT	53	54	52	53	52	53	…	…	…	…	…	…
	ST	…	…	…	…	…	…	…	…	…	…	…	…
F_su, ksi	L	37	38	37	38	37	38	…	…	…	…	…	…
	LT	37	38	37	38	37	38	…	…	…	…	…	…
	ST	…	…	…	…	37	38	…	…	…	…	…	…
F_bru (e/D = 1.5), ksi	L	99	100	99	100	99	100	…	…	…	…	…	…
	LT	99	100	99	100	99	100	…	…	…	…	…	…
	ST	…	…	…	…	99	100	…	…	…	…	…	…
F_bru (e/D = 2.0), ksi	L	126	128	126	128	126	128	…	…	…	…	…	…
	LT	126	128	126	128	126	128	…	…	…	…	…	…
	ST	…	…	…	…	126	128	…	…	…	…	…	…
F_bry (e/D = 1.5), ksi	L	82	83	82	83	82	83	…	…	…	…	…	…
	LT	82	83	82	83	82	83	…	…	…	…	…	…
	ST	…	…	…	…	82	83	…	…	…	…	…	…
F_bry (e/D = 2.0), ksi	L	94	96	94	96	94	96	…	…	…	…	…	…
	LT	94	96	94	96	94	96	…	…	…	…	…	…
	ST	…	…	…	…	94	96	…	…	…	…	…	…
e, %	L	…	…	…	…	…	…	…	…	…	…	…	…
	LT	7	7	6	6	6	6	6	6	4	4	3	3
	ST	…	…	…	…	…	…	…	…	…	…	…	…
E, Msi		10.5	10.5	10.5	10.5	10.5	10.5	10.5	10.5	10.5	10.5	…	…
E_c, Msi		10.8	10.8	10.8	10.8	10.8	10.8	10.8	10.8	10.8	10.8	…	…
G, Msi		4	4	4	4	4	4	4	4	4	4	…	…
ν		0.33	0.33	0.33	0.33	0.33	0.33	0.33	0.33	0.33	0.33	…	…
ρ, lb/in3		0.103	0.103	0.103	0.103	0.103	0.103	0.103	0.103	0.103	0.103	…	…

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Strength allowables at temperature, percent of room temperature

°F	F_tu	F_ty
-300	119.5	117.2
-200	109.1	110.1
-100	106.4	106
0	103.7	102.7
100	98.7	98.6
200	90.7	91.2
300	79.2	79.1
400	61.2	61.3
500	41.7	42.1
600	30.8	30.6
700	15	14.5
800	4.7	4.5

Factors in percent of the room-temperature allowable.

Other 2219 Tables

2219-T62 Sheet and plate (Table 3.2.8.0(b))
2219-T81 Sheet and plate (Table 3.2.8.0(b))
2219-T851 Sheet and plate (Table 3.2.8.0(b))
2219-T8511 Extruded shapes (Table 3.2.8.0(d))
2219-T852 Hand Forging (Table 3.2.8.0(c))
2219-T87 Sheet (Table 3.2.8.0(b))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.