Tools › Materials › Titanium › Ti-6Al-4V-Solution treated and aged Round, square, and hexagon bar

Ti-6Al-4V-Solution treated and aged Round, square, and hexagon bar: MIL-HDBK-5J Design Allowables

show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Material class	Titanium
Alloy / temper / form	Ti-6Al-4V / Solution treated and aged / Round, square, and hexagon bar
Specifications	MIL-T-9047
Handbook	MIL-HDBK-5J, 31 January 2003, section 5.4.1.0, Table 5.4.1.0(d) (pdf page 56 of the chapter file)
Dimension bands	5
Density	4429 kg/m³

Design Mechanical and Physical Properties (room temperature)

Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Dimension band		0.000–0.500 in (0–12.7 mm)	0.501–1.000 in (12.73–25.4 mm)	1.001–1.500 in (25.43–38.1 mm)	1.501–2.000 in (38.13–50.8 mm)	2.001–3.000 in (50.83–76.2 mm)
Specification		MIL-T-9047	MIL-T-9047	MIL-T-9047	MIL-T-9047	MIL-T-9047
Basis		S	S	S	S	S
F_tu, MPa	L	1138	1103	1069	1034	965.3
F_tu, MPa	LT	1138	1103	1069	1034	965.3
F_ty, MPa	L	1069	1034	999.7	965.3	896.3
F_ty, MPa	LT	1069	1034	999.7	965.3	896.3
e, %	L	10	10	10	10	10
e, %	LT	10	10	10	10	10
E, GPa		116.5	116.5	116.5	116.5	116.5
E_c, GPa		118.6	118.6	118.6	118.6	118.6
G, GPa		42.75	42.75	42.75	42.75	42.75
ν		0.31	0.31	0.31	0.31	0.31
ρ, kg/m³		4429	4429	4429	4429	4429

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Strength allowables at temperature, percent of room temperature

Moduli at temperature

°C	F_cy	F_su	F_bru	F_bry
38	97.4	97.4	98	98
93	86.5	91.6	91.6	91.6
149	77.4	85.7	85.5	85.5
204	69.8	80.3	80	80
26	64.6	76.9	76.5	76.5
316	63.4	74.4	75.6	75.6
371	62.4	72.9	74.4	74.4
427	59.6	69.4	72.1	72.1
538			53.7	53.7

Factors in percent of the room-temperature allowable.

Other Ti-6Al-4V Tables

Ti-6Al-4V-Alpha-beta or beta processed, / annealed Die forging (Table 5.4.1.0(f))
Ti-6Al-4V-Alpha-beta processed, annealed Die forging (Table 5.4.1.0(f))
Ti-6Al-4V-Annealed Bar (Table 5.4.1.0(c))
Ti-6Al-4V-Annealed Extrusion (Table 5.4.1.0(e))
Ti-6Al-4V-Annealed HIP Casting (Table 5.4.1.0(g))
Ti-6Al-4V-Annealed Plate (Table 5.4.1.0(b))
Ti-6Al-4V-Annealed Sheet (Table 5.4.1.0(b))
Ti-6Al-4V-Solution treated and aged Extrusion (Table 5.4.1.0(e))
Ti-6Al-4V-Solution treated and aged Rectangular bar (Table 5.4.1.0(d))
Ti-6Al-4V-Solution treated and aged Sheet, strip, and plate (Table 5.4.1.0(b))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.