Tools › Materials › Steel › 17-4PH-H1150 Forging, tubing, and rings

17-4PH-H1150 Forging, tubing, and rings: MIL-HDBK-5J Design Allowables

show SI units (MPa, GPa, kg/m³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Material class	Steel
Alloy / temper / form	17-4PH / H1150 / Forging, tubing, and rings
Specifications	AMS 5643
Handbook	MIL-HDBK-5J, 31 January 2003, section 2.6.9.0, Table 2.6.9.0(d) (pdf page 198 of the chapter file)
Dimension bands	1
Density	0.284 lb/in3

Design Mechanical and Physical Properties (room temperature)

As printed in the handbook table. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Dimension band		0–8 in
Specification		AMS 5643
Basis		S
F_tu, ksi	L	135
F_ty, ksi	L	105
e, %	L	16
E, Msi		28.5
E_c, Msi		30
G, Msi		11.2
ν		0.27
ρ, lb/in3		0.284

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Strength allowables at temperature, percent of room temperature

°F	F_tu	F_ty
100	98.9	99.2
200	95.8	97.4
300	93	95.4
400	90.1	93.5
500	87.2	91.5
600	84.1	89.9
700	81.4	87.2
800	77.7	83.5
1000	65.8	68.7

Factors in percent of the room-temperature allowable.

Other 17-4PH Tables

17-4PH Investment Casting (Table 2.6.9.0(f))
17-4PH-H1000 Investment Casting (Table 2.6.9.0(f))
17-4PH-H1025 Bar (Table 2.6.9.0(e))
17-4PH-H1025 Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H1025 Sheet, strip, and plate (Table 2.6.9.0(b))
17-4PH-H1075 Bar (Table 2.6.9.0(e))
17-4PH-H1075 Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H1075 Sheet, strip, and plate (Table 2.6.9.0(b))
17-4PH-H1100 Bar (Table 2.6.9.0(e))
17-4PH-H1100 Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H1100 Investment Casting (Table 2.6.9.0(f))
17-4PH-H1100 Sheet, strip, and plate (Table 2.6.9.0(b))
17-4PH-H1150 Bar (Table 2.6.9.0(e))
17-4PH-H1150 Sheet, strip, and plate (Table 2.6.9.0(b))
17-4PH-H1150Ma Bar (Table 2.6.9.0(e))
17-4PH-H1150Ma Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H900 Bar (Table 2.6.9.0(e))
17-4PH-H900 Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H900 Sheet, strip, and plate (Table 2.6.9.0(b))
17-4PH-H925 Bar (Table 2.6.9.0(e))
17-4PH-H925 Forging, tubing, and rings (Table 2.6.9.0(d))
17-4PH-H925 Sheet, strip, and plate (Table 2.6.9.0(b))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.