7075-T76 Sheet and plate: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Aluminum |
| Alloy / temper / form | 7075 / T76 / Sheet and plate |
| Specifications | AMS-QQ-A-250/24 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 3.7.6.0, Table 3.7.6.0(b) (pdf page 374 of the chapter file) |
| Dimension bands | 1 |
| Density | 2796 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.063–0.249 in (1.6–6.325 mm) | |
|---|---|---|
| Specification | AMS-QQ-A-250/24 | |
| Basis | S | |
| Ftu, MPa | L | 496.4 |
| LT | 503.3 | |
| Fty, MPa | L | 427.5 |
| LT | 427.5 | |
| Fcy, MPa | L | 420.6 |
| LT | 448.2 | |
| Fsu, MPa | L | 289.6 |
| LT | 289.6 | |
| Fbru (e/D = 1.5), MPa | L | 772.2 |
| LT | 772.2 | |
| Fbru (e/D = 2.0), MPa | L | 999.7 |
| LT | 999.7 | |
| Fbry (e/D = 1.5), MPa | L | 606.7 |
| LT | 606.7 | |
| Fbry (e/D = 2.0), MPa | L | 703.3 |
| LT | 703.3 | |
| e, % | L | … |
| LT | 8 | |
| E, GPa | 71.02 | |
| Ec, GPa | 72.39 | |
| G, GPa | 26.89 | |
| ν | 0.33 | |
| ρ, kg/m³ | 2796 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Moduli at temperature
Other 7075 Tables
- 7075-T6 Clad sheet (Table 3.7.6.0(c))
- 7075-T6 Die forging (Table 3.7.6.0(e))
- 7075-T6 Hand forging (Table 3.7.6.0(f))
- 7075-T6 and T62 Clad sheet (Table 3.7.6.0(c))
- 7075-T6 and T62 Sheet (Table 3.7.6.0(b))
- 7075-T6, T651, and T62 Bar, rod, and shapes: rolled, drawn, or cold-finished (Table 3.7.6.0(d))
- 7075-T6, T6510, T6511, and T62 Extrusion (rod, bar, and shapes) (Table 3.7.6.0(g))
- 7075-T62 Clad plate (Table 3.7.6.0(c))
- 7075-T62 Plate (Table 3.7.6.0(b))
- 7075-T651 Clad plate (Table 3.7.6.0(c))
- 7075-T651 Plate (Table 3.7.6.0(b))
- 7075-T652 Die forging (Table 3.7.6.0(e))
- 7075-T652 Hand forging (Table 3.7.6.0(f))
- 7075-T73 Hand forging (Table 3.7.6.0(f))
- 7075-T73 Sheet (Table 3.7.6.0(b))
- 7075-T7351 Plate (Table 3.7.6.0(b))
- 7075-T7352 Die forging (Table 3.7.6.0(e))
- 7075-T7352 Hand forging (Table 3.7.6.0(f))
- 7075-T73a, T73510, T73511 Extrusion (rod, bars, and shapes) (Table 3.7.6.0(g))
- 7075-T73a,b Die forging (Table 3.7.6.0(e))
- 7075-T73b or T7351 Bar, rod, and shapes: rolled, drawn, or cold-finished (Table 3.7.6.0(d))
- 7075-T76 Clad sheet (Table 3.7.6.0(c))
- 7075-T76, T76510, T76511 Extrusion (rod, bar, and shapes) (Table 3.7.6.0(g))
- 7075-T7651 Clad plate (Table 3.7.6.0(c))
- 7075-T7651 Sheet and plate (Table 3.7.6.0(b))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.