6061-T62 Extruded rod, bar, and shapes: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Aluminum |
| Alloy / temper / form | 6061 / T62 / Extruded rod, bar, and shapes |
| Specifications | AMS 4160 & AMS-QQ-A-200/8 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 3.6.2.0, Table 3.6.2.0(g) (pdf page 272 of the chapter file) |
| Dimension bands | 1 |
| Density | 2713 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | all | |
|---|---|---|
| Specification | AMS 4160 & AMS-QQ-A-200/8 | |
| Basis | S | |
| Ftu, MPa | L | 262 |
| Fty, MPa | L | 241.3 |
| e, % | L | 10 |
| E, GPa | 68.26 | |
| Ec, GPa | 69.64 | |
| G, GPa | 26.2 | |
| ν | 0.33 | |
| ρ, kg/m³ | 2713 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Moduli at temperature
Other 6061 Tables
- 6061-T4 Drawn tube (Table 3.6.2.0(c))
- 6061-T4 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T4 Sheet (Table 3.6.2.0(b))
- 6061-T4, T4510, / and T4511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Drawn tube (Table 3.6.2.0(c))
- 6061-T42 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Plate (Table 3.6.2.0(b))
- 6061-T42 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T42 Sheet (Table 3.6.2.0(b))
- 6061-T451 Plate (Table 3.6.2.0(b))
- 6061-T451 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 and T62 Sheet (Table 3.6.2.0(b))
- 6061-T6 and T652 Die forging (Table 3.6.2.0(e))
- 6061-T6, T6510, and T6511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T62 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 and T62 Plate (Table 3.6.2.0(b))
- 6061-T6a and T652 Hand forging (Table 3.6.2.0(f))
- 6061-T6b and T62 Drawn tube (Table 3.6.2.0(c))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.