6061-T451 Plate: MIL-HDBK-5J Design Allowables
show SI units (MPa, GPa, kg/m³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Aluminum |
| Alloy / temper / form | 6061 / T451 / Plate |
| Specifications | AMS 4026 and AMS-QQ-A-250/11 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 3.6.2.0, Table 3.6.2.0(b) (pdf page 265 of the chapter file) |
| Dimension bands | 2 |
| Density | 0.098 lb/in3 |
Design Mechanical and Physical Properties (room temperature)
As printed in the handbook table. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.250–2.000 in | 2.001–3.000 in | |||
|---|---|---|---|---|---|
| Specification | AMS 4026 and AMS-QQ-A-250/11 | AMS 4026 and AMS-QQ-A-250/11 | |||
| Basis | A | B | A | B | |
| Ftu, ksi | LT | 30 | 32 | 30 | 32 |
| Fty, ksi | LT | 16 | 18 | 16 | 18 |
| Fcy, ksi | LT | 16 | 18 | 38 | 38 |
| Fsu, ksi | LT | 20 | 21 | … | … |
| Fbru (e/D = 1.5), ksi | LT | 48 | 52 | … | … |
| Fbru (e/D = 2.0), ksi | LT | 63 | 67 | … | … |
| Fbry (e/D = 1.5), ksi | LT | 22 | 25 | … | … |
| Fbry (e/D = 2.0), ksi | LT | 26 | 29 | … | … |
| E, Msi | 9.9 | 9.9 | 9.9 | 9.9 | |
| Ec, Msi | 10.1 | 10.1 | 10.1 | 10.1 | |
| G, Msi | 3.8 | 3.8 | 3.8 | 3.8 | |
| ν | 0.33 | 0.33 | 0.33 | 0.33 | |
| ρ, lb/in3 | 0.098 | 0.098 | 0.098 | 0.098 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Moduli at temperature
Other 6061 Tables
- 6061-T4 Drawn tube (Table 3.6.2.0(c))
- 6061-T4 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T4 Sheet (Table 3.6.2.0(b))
- 6061-T4, T4510, / and T4511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Drawn tube (Table 3.6.2.0(c))
- 6061-T42 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Plate (Table 3.6.2.0(b))
- 6061-T42 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T42 Sheet (Table 3.6.2.0(b))
- 6061-T451 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 and T62 Sheet (Table 3.6.2.0(b))
- 6061-T6 and T652 Die forging (Table 3.6.2.0(e))
- 6061-T6, T6510, and T6511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T62 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T62 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 and T62 Plate (Table 3.6.2.0(b))
- 6061-T6a and T652 Hand forging (Table 3.6.2.0(f))
- 6061-T6b and T62 Drawn tube (Table 3.6.2.0(c))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.