6061-T42 Plate: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Aluminum |
| Alloy / temper / form | 6061 / T42 / Plate |
| Specifications | AMS-QQ-A-250/11 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 3.6.2.0, Table 3.6.2.0(b) (pdf page 265 of the chapter file) |
| Dimension bands | 2 |
| Density | 2713 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.250–1.000 in (6.35–25.4 mm) | 1.001–3.000 in (25.43–76.2 mm) | |
|---|---|---|---|
| Specification | AMS-QQ-A-250/11 | AMS-QQ-A-250/11 | |
| Basis | S | S | |
| Ftu, MPa | LT | 206.8 | 206.8 |
| Fty, MPa | LT | 96.53 | 96.53 |
| Fcy, MPa | LT | 262 | 262 |
| E, GPa | 68.26 | 68.26 | |
| Ec, GPa | 69.64 | 69.64 | |
| G, GPa | 26.2 | 26.2 | |
| ν | 0.33 | 0.33 | |
| ρ, kg/m³ | 2713 | 2713 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Moduli at temperature
Other 6061 Tables
- 6061-T4 Drawn tube (Table 3.6.2.0(c))
- 6061-T4 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T4 Sheet (Table 3.6.2.0(b))
- 6061-T4, T4510, / and T4511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Drawn tube (Table 3.6.2.0(c))
- 6061-T42 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T42 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T42 Sheet (Table 3.6.2.0(b))
- 6061-T451 Plate (Table 3.6.2.0(b))
- 6061-T451 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T6 and T62 Sheet (Table 3.6.2.0(b))
- 6061-T6 and T652 Die forging (Table 3.6.2.0(e))
- 6061-T6, T6510, and T6511 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T62 Extruded rod, bar, and shapes (Table 3.6.2.0(g))
- 6061-T62 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 Rolled, drawn, or cold-finished rod and special shapes (Table 3.6.2.0(d))
- 6061-T651 and T62 Plate (Table 3.6.2.0(b))
- 6061-T6a and T652 Hand forging (Table 3.6.2.0(f))
- 6061-T6b and T62 Drawn tube (Table 3.6.2.0(c))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.