Tools › Materials › Aluminum › 2024-T361 Plate

2024-T361 Plate: MIL-HDBK-5J Design Allowables

show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Material class	Aluminum
Alloy / temper / form	2024 / T361 / Plate
Specifications	AMS-QQ-A-250/4
Handbook	MIL-HDBK-5J, 31 January 2003, section 3.2.3.0, Table 3.2.3.0(b) (pdf page 71 of the chapter file)
Dimension bands	1
Density	2768 kg/m³

Design Mechanical and Physical Properties (room temperature)

Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Dimension band		0.250–0.500 in (6.35–12.7 mm)
Specification		AMS-QQ-A-250/4
Basis		S
F_tu, MPa	L	461.9
F_tu, MPa	LT	455.1
F_ty, MPa	L	372.3
F_ty, MPa	LT	337.8
F_cy, MPa	L	317.2
F_cy, MPa	LT	358.5
F_su, MPa	L	282.7
F_su, MPa	LT	282.7
F_bru (e/D = 1.5), MPa	L	751.5
F_bru (e/D = 1.5), MPa	LT	751.5
F_bru (e/D = 2.0), MPa	L	930.8
F_bru (e/D = 2.0), MPa	LT	930.8
F_bry (e/D = 1.5), MPa	L	558.5
F_bry (e/D = 1.5), MPa	LT	558.5
F_bry (e/D = 2.0), MPa	L	661.9
F_bry (e/D = 2.0), MPa	LT	661.9
e, %	L	…
e, %	LT	9
E, GPa		73.77
E_c, GPa		75.15
G, GPa		27.58
ν		0.33
ρ, kg/m³		2768

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Moduli at temperature

Other 2024 Tables

2024-T3 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T3 Drawn tubing (Table 3.2.3.0(g))
2024-T3 Sheet (Table 3.2.3.0(b))
2024-T3, T3510, and T3511 Extruded bar, rod, and shapes (Table 3.2.3.0(j))
2024-T351 Bar and rod; rolled, drawn, or cold-finished (Table 3.2.3.0(i))
2024-T351 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T351 Plate (Table 3.2.3.0(b))
2024-T361 Bar and rod; rolled, drawn, or cold-finished (Table 3.2.3.0(i))
2024-T361 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T361 Sheet (Table 3.2.3.0(b))
2024-T4 Bar and rod; rolled, drawn, or cold-finished (Table 3.2.3.0(i))
2024-T4 Clad coiled sheet (Table 3.2.3.0(e))
2024-T4 Coiled Sheet (Table 3.2.3.0(b))
2024-T42 Bar and rod; rolled, drawn, or cold-finished (Table 3.2.3.0(i))
2024-T42 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T42 Drawn tubing (Table 3.2.3.0(g))
2024-T42 Extruded bar, rod, and shapes (Table 3.2.3.0(j))
2024-T42 Flat Sheet and Plate (Table 3.2.3.0(b))
2024-T6 Bar and rod; rolled, drawn, or cold finished (Table 3.2.3.0(i))
2024-T62 Bar and rod; rolled, drawn, or cold finished (Table 3.2.3.0(i))
2024-T62 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T62 Flat Sheet and Plate (Table 3.2.3.0(b))
2024-T72 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T72 Flat Sheet and Plate (Table 3.2.3.0(b))
2024-T81 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T81 Drawn tubing (Table 3.2.3.0(g))
2024-T81 Sheet (Table 3.2.3.0(b))
2024-T81, T8510, and T8511 Extruded bar, rod, and shapes (Table 3.2.3.0(j))
2024-T851 Bar and rod; rolled, drawn, or cold finished (Table 3.2.3.0(i))
2024-T851 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T851 Plate (Table 3.2.3.0(b))
2024-T861 Clad flat sheet and plate (Table 3.2.3.0(e))
2024-T861 Plate (Table 3.2.3.0(b))
2024-T861 Sheet (Table 3.2.3.0(b))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.