2014-T62 Plate: MIL-HDBK-5J Design Allowables

show SI units (MPa, GPa, kg/m³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Material class	Aluminum
Alloy / temper / form	2014 / T62 / Plate
Specifications	AMS 4028
Handbook	MIL-HDBK-5J, 31 January 2003, section 3.2.1.0, Table 3.2.1.0(b) (pdf page 29 of the chapter file)
Dimension bands	2
Density	0.101 lb/in3

Design Mechanical and Physical Properties (room temperature)

As printed in the handbook table. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Dimension band		0.250–0.499 in		0.500–1.000 in
Specification		AMS 4028		AMS 4028
Basis		A	B	A	B
F_tu, ksi	L	65	67	65	67
F_tu, ksi	LT	67	69	67	69
F_ty, ksi	L	57	59	57	59
F_ty, ksi	LT	59	61	59	61
F_cy, ksi	L	59	61	59	61
F_cy, ksi	LT	60	62	60	62
F_su, ksi	L	37	39	37	39
F_su, ksi	LT	37	39	37	39
F_bru (e/D = 1.5), ksi	L	100	103	100	103
F_bru (e/D = 1.5), ksi	LT	100	103	100	103
F_bru (e/D = 2.0), ksi	L	127	131	127	131
F_bru (e/D = 2.0), ksi	LT	127	131	127	131
F_bry (e/D = 1.5), ksi	L	84	87	84	87
F_bry (e/D = 1.5), ksi	LT	84	87	84	87
F_bry (e/D = 2.0), ksi	L	99	103	99	103
F_bry (e/D = 2.0), ksi	LT	99	103	99	103
e, %	L	…	…	…	…
e, %	LT	7	7	6	6
E, Msi		10.7	10.7	10.7	10.7
E_c, Msi		10.9	10.9	10.9	10.9
G, Msi		4	4	4	4
ν		0.33	0.33	0.33	0.33
ρ, lb/in3		0.101	0.101	0.101	0.101

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Moduli at temperature

Other 2014 Tables

2014-T6 Clad sheet (Table 3.2.1.0(c))
2014-T6 Die forging (Table 3.2.1.0(e))
2014-T6 Hand forging (Table 3.2.1.0(f))
2014-T6 Sheet (Table 3.2.1.0(b))
2014-T6 and T651 Bar, rod, and shapes, rolled, drawn, or cold-finished (Table 3.2.1.0(d))
2014-T6, T6510, and T6511 Extruded bar, rod, and shapes (Table 3.2.1.0(g))
2014-T62 Bar, rod, and shapes, rolled, drawn, or cold-finished (Table 3.2.1.0(d))
2014-T62 Clad plate (Table 3.2.1.0(c))
2014-T62 Clad sheet (Table 3.2.1.0(c))
2014-T62 Extruded bar, rod, and shapes (Table 3.2.1.0(g))
2014-T62 Sheet (Table 3.2.1.0(b))
2014-T651 Clad plate (Table 3.2.1.0(c))
2014-T651 Plate (Table 3.2.1.0(b))
2014-T652 Die forging (Table 3.2.1.0(e))
2014-T652 Hand forging (Table 3.2.1.0(f))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.