2014-T62 Clad plate: MIL-HDBK-5J Design Allowables

show SI units (MPa, GPa, kg/m³) open the MIL-HDBK-5J tool compare against temperature find alternatives

Design Mechanical and Physical Properties (room temperature)

As printed in the handbook table. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.

Effect of Temperature

Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.

Moduli at temperature

Other 2014 Tables

• 2014-T6 Clad sheet (Table 3.2.1.0(c))
• 2014-T6 Die forging (Table 3.2.1.0(e))
• 2014-T6 Hand forging (Table 3.2.1.0(f))
• 2014-T6 Sheet (Table 3.2.1.0(b))
• 2014-T6 and T651 Bar, rod, and shapes, rolled, drawn, or cold-finished (Table 3.2.1.0(d))
• 2014-T6, T6510, and T6511 Extruded bar, rod, and shapes (Table 3.2.1.0(g))
• 2014-T62 Bar, rod, and shapes, rolled, drawn, or cold-finished (Table 3.2.1.0(d))
• 2014-T62 Clad sheet (Table 3.2.1.0(c))
• 2014-T62 Extruded bar, rod, and shapes (Table 3.2.1.0(g))
• 2014-T62 Plate (Table 3.2.1.0(b))
• 2014-T62 Sheet (Table 3.2.1.0(b))
• 2014-T651 Clad plate (Table 3.2.1.0(c))
• 2014-T651 Plate (Table 3.2.1.0(b))
• 2014-T652 Die forging (Table 3.2.1.0(e))
• 2014-T652 Hand forging (Table 3.2.1.0(f))

Source and Use

U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.