Ti-13V-11Cr-3Al-Annealed Sheet, strip, and plate: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Titanium |
| Alloy / temper / form | Ti-13V-11Cr-3Al / Annealed / Sheet, strip, and plate |
| Specifications | AMS-T-9046, Comp. B-1 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 5.5.1.0, Table 5.5.1.0(b) (pdf page 120 of the chapter file) |
| Dimension bands | 2 |
| Density | 4816 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.012–0.049 in (0.3048–1.245 mm) | 0.050–4.000 in (1.27–101.6 mm) | |
|---|---|---|---|
| Specification | AMS-T-9046, Comp. B-1 | AMS-T-9046, Comp. B-1 | |
| Basis | S | S | |
| Ftu, MPa | L | 910.1 | 861.8 |
| LT | 910.1 | 861.8 | |
| ST | … | 861.8 | |
| Fty, MPa | L | 868.7 | 827.4 |
| LT | 868.7 | 827.4 | |
| ST | … | 827.4 | |
| Fcy, MPa | L | … | 827.4 |
| LT | … | 827.4 | |
| ST | … | 827.4 | |
| Fsu, MPa | L | … | 634.3 |
| LT | … | 634.3 | |
| ST | … | 634.3 | |
| Fbru (e/D = 1.5), MPa | L | … | 1427 |
| LT | … | 1427 | |
| ST | … | 1427 | |
| Fbru (e/D = 2.0), MPa | L | … | 1862 |
| LT | … | 1862 | |
| ST | … | 1862 | |
| Fbry (e/D = 1.5), MPa | L | … | 1165 |
| LT | … | 1165 | |
| ST | … | 1165 | |
| Fbry (e/D = 2.0), MPa | L | … | 1379 |
| LT | … | 1379 | |
| ST | … | 1379 | |
| e, % | L | 8 | 10 |
| LT | 8 | 10 | |
| ST | … | 10 | |
| E, GPa | 99.97 | 99.97 | |
| ρ, kg/m³ | 4816 | 4816 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Strength allowables at temperature, percent of room temperature
Moduli at temperature
| °C | F_tu | F_ty | F_cy | F_su | F_bru | F_bry | F_bry (e/D = 2.0) |
|---|---|---|---|---|---|---|---|
| 38 | 97.2 | 97.2 | 96.5 | 98.3 | 98.4 | 97 | 97 |
| 93 | 88.5 | 88.5 | 88.4 | 94.4 | 92.5 | 91 | 91 |
| 149 | 83.7 | 86.3 | 84.4 | 91.6 | 89.3 | 89.8 | 89.8 |
| 204 | 81.3 | 85.4 | 81.8 | 89.5 | 87.3 | 89.3 | 89.3 |
| 26 | 79.3 | 83.9 | 79.8 | 87.9 | 86 | 84.5 | 88.6 |
| 316 | 77.3 | 82.5 | 78.2 | 86.4 | 85.5 | 85.3 | 88 |
| 371 | 75.3 | 81.6 | 76.5 | 85.4 | 84.5 | 86.1 | 87.1 |
| 427 | 73 | 79.8 | 75.4 | 83.2 | 82.9 | 86.2 | 84.3 |
Factors in percent of the room-temperature allowable.
Other Ti-13V-11Cr-3Al Tables
- Ti-13V-11Cr-3Al-Annealed Bar (Table 5.5.1.0(b))
- Ti-13V-11Cr-3Al-Solution treated / and aged Bar (Table 5.5.1.0(b))
- Ti-13V-11Cr-3Al-Solution treated / and aged Sheet, strip, and plate (Table 5.5.1.0(b))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.