AM-355-SCT850 Sheet and strip: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Steel |
| Alloy / temper / form | AM-355 / SCT850 / Sheet and strip |
| Specifications | AMS 5547 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 2.6.2.0, Table 2.6.2.0(c) (pdf page 123 of the chapter file) |
| Dimension bands | 1 |
| Density | 7806 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.001–0.187 in (0.0127–4.75 mm) | |
|---|---|---|
| Specification | AMS 5547 | |
| Basis | S | |
| Ftu, MPa | L | 1296 |
| LT | 1310 | |
| Fty, MPa | L | 1117 |
| LT | 1138 | |
| Fcy, MPa | L | 1241 |
| LT | … | |
| Fsu, MPa | L | 854.9 |
| LT | 854.9 | |
| Fbru (e/D = 2.0), MPa | L | 2641 |
| LT | 2641 | |
| Fbry (e/D = 2.0), MPa | L | 1917 |
| LT | 1917 | |
| e, % | L | 10 |
| LT | 10 | |
| E, GPa | 199.9 | |
| Ec, GPa | 199.9 | |
| G, GPa | 75.84 | |
| ν | 0.32 | |
| ρ, kg/m³ | 7806 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Strength allowables at temperature, percent of room temperature
Moduli at temperature
| °C | F_su |
|---|---|
| 38 | 94.3 |
| 93 | 84.9 |
| 149 | 81.7 |
| 204 | 79.9 |
| 26 | 78.1 |
| 316 | 76.3 |
| 371 | 74.6 |
| 427 | 72.8 |
Factors in percent of the room-temperature allowable.
Other AM-355 Tables
- AM-355-SCT 1000 Plate (Table 2.6.2.0(d))
- AM-355-SCT1000 Bar and forging (Table 2.6.2.0(c))
- AM-355-SCT1000 Sheet and strip (Table 2.6.2.0(c))
- AM-355-SCT850 Bar and forging (Table 2.6.2.0(c))
- AM-355-SCT850 Plate (Table 2.6.2.0(d))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.