Waspaloy-Solution, stabilization, and precipitation heat tr Bar, forging, and / ring: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Heat-Resistant |
| Alloy / temper / form | Waspaloy / Solution, stabilization, and precipitation heat tr / Bar, forging, and / ring |
| Specifications | AMS 5706 and AMS 5707 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 6.3.8.0, Table 6.3.8.0(b) (pdf page 91 of the chapter file) |
| Dimension bands | 1 |
| Density | 8249 kg/m³ |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.000–3.500 in (0–88.9 mm) | |
|---|---|---|
| Specification | AMS 5706 and AMS 5707 | |
| Basis | S | |
| Ftu, MPa | L | 1103 |
| Fty, MPa | L | 758.4 |
| e, % | L | 15 |
| E, GPa | 211 | |
| ρ, kg/m³ | 8249 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Strength allowables at temperature, percent of room temperature
| °C | F_tu | F_ty |
|---|---|---|
| 38 | 98.9 | 98.9 |
| 93 | 96.8 | 96.8 |
| 149 | 94.2 | 95.5 |
| 204 | 93.7 | 92.5 |
| 26 | 92 | 90.5 |
| 316 | 89.8 | 89.8 |
| 371 | 88.3 | 88.3 |
| 427 | 86.9 | 86.9 |
| 538 | 84 | 84 |
| 649 | 80 | 80 |
Factors in percent of the room-temperature allowable.
Other Waspaloy Tables
- Waspaloy-Solution, stabilization, and precipitation heat tr Forging (Table 6.3.8.0(b))
- Waspaloy-Solution, stabilization, and precipitation heat tr Sheet, strip, and plate (Table 6.3.8.0(b))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.