Ren� 41-Solution treated and aged (1400 F) Plate: MIL-HDBK-5J Design Allowables
show US units (ksi, Msi, lb/in³) open the MIL-HDBK-5J tool compare against temperature find alternatives
| Material class | Heat-Resistant |
| Alloy / temper / form | Ren� 41 / Solution treated and aged (1400 F) / Plate |
| Specifications | AMS 5545 |
| Handbook | MIL-HDBK-5J, 31 January 2003, section 6.3.7.0, Table 6.3.7.0(b) (pdf page 84 of the chapter file) |
| Dimension bands | 1 |
Design Mechanical and Physical Properties (room temperature)
Converted from the handbook table (ksi, Msi, lb/in³) and rounded to 4 significant figures; dimension bands in inches with mm in parentheses. Bases: A and B are statistical minimums (99 % and 90 % probability at 95 % confidence), S the specification minimum. Grain directions: L longitudinal, LT long transverse, ST short transverse.
| Dimension band | 0.188–0.375 in (4.775–9.525 mm) | |
|---|---|---|
| Specification | AMS 5545 | |
| Basis | S | |
| Ftu, MPa | LT | 1172 |
| Fty, MPa | LT | 896.3 |
| Fsu, MPa | LT | 723.9 |
| Fbru (e/D = 1.5), MPa | LT | 1682 |
| Fbru (e/D = 2.0), MPa | LT | 2137 |
| Fbry (e/D = 1.5), MPa | LT | 1434 |
| Fbry (e/D = 2.0), MPa | LT | 1786 |
| e, % | LT | 10 |
| E, GPa | 217.9 | |
| Ec, GPa | 217.9 | |
| G, GPa | 83.43 | |
| ν | 0.31 | |
Effect of Temperature
Percent of the room-temperature value against temperature, digitized from the handbook figures (the shortest exposure of each figure, every 10 °F). Strength curves give the allowable at temperature; "after exposure" curves give the room-temperature property after a soak at that temperature.
Strength allowables at temperature, percent of room temperature
Moduli at temperature
Elongation and exposure effects
| °C | F_tu | F_ty | F_cy | F_su | F_bru | F_bru (e/D = 2.0) |
|---|---|---|---|---|---|---|
| 38 | 99.6 | 99.6 | 99.3 | 99.3 | ||
| 93 | 96.3 | 96.3 | 95.9 | 95.9 | ||
| 149 | 94.2 | 94.2 | 93 | 93 | ||
| 204 | 92.3 | 92.3 | 90.5 | 90.5 | 93.2 | |
| 26 | 90.2 | 90.2 | 88.7 | 88.7 | 91.9 | |
| 316 | 89 | 89 | 87.3 | 87.3 | 90.9 | |
| 371 | 88.4 | 88.4 | 86.3 | 86.3 | 89.9 | 84.9 |
| 427 | 87.7 | 87.7 | 85.4 | 85.4 | 89 | 83.6 |
| 538 | 86.1 | 86.1 | 83.8 | 83.8 | ||
| 649 | 84.4 | 84.4 | 82.3 | 82.4 |
Factors in percent of the room-temperature allowable.
Other Ren� 41 Tables
- Ren� 41-Solution treated and aged (1400 F) Bar and forging (Table 6.3.7.0(b))
- Ren� 41-Solution treated and aged (1400 F) Sheet (Table 6.3.7.0(b))
Source and Use
U.S. Department of Defense (2003). Metallic Materials and Elements for Aerospace Vehicle Structures. MIL-HDBK-5J, 31 January 2003 (public domain). The values are the handbook's design allowables as extracted from the chapter tables; check the printed table before use in a certified analysis, and note that MIL-HDBK-5J was superseded by MMPDS, whose later editions may differ. No warranty is given.